Method of forming a capacitor

ABSTRACT

A conductive structure, including an adhesion layer and a conductor in contact with the adhesion layer and having a thickness of less than six hundred Angstroms. The present invention may be used to form a capacitor, including an adhesion layer, a first conductor in contact with the adhesion layer and having a thickness of less than six hundred Angstroms, a second conductor, and a dielectric between the first and second conductors. The present invention is also directed towards structures wherein iridium or rhodium may be used in place of the combination of the adhesion layer and conductor.

CROSS REFERENCE TO RELATED APPLICATIONS

[0001] Not Applicable.

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT

[0002] Not Applicable.

BACKGROUND OF THE INVENTION

[0003] 1. Field of the Invention

[0004] The present invention is directed generally to a structure havingthin films that does not exhibit spotting and non-wettingcharacteristics and, more particularly, to a structure having thin filmsthat may include an adhesion layer.

[0005] 21. Description of the Background

[0006] Films used in integrated circuits are becoming thinner as minimumfeature sizes decrease and as the competitive nature of integratedcircuit fabrication forces manufactures to produce smaller parts (i.e.die) in order to produce smaller and less expensive integrated circuits.

[0007] A result of decreasing film thickness is that some materials willnot form a conformal film below certain thicknesses. Instead, thosematerials exhibit “spotting” or “non-wetting” characteristics wherebythe material forms “islands” separated by gaps where the material willnot form. One example of such a material is platinum, which exhibitsspotting when formed on silicon at a thickness less than about sixhundred (600) Angstroms and then annealed to 700° C.

[0008] Platinum, as well as other materials, is important when formingintegrated circuits because it exhibits desirable characteristics duringfabrication steps. For example, platinum does not readily form an oxideduring annealing in oxygen.

[0009] Therefore, the need exists for a structure having thin films thatdoes not exhibit spotting or non-wetting characteristics.

BRIEF SUMMARY OF THE INVENTION

[0010] The present invention is directed to a conductive structureincluding an adhesion layer and a conductor in contact with the adhesionlayer and having a thickness of less than six hundred Angstroms. Thepresent invention may be used to form devices, such as capacitors. Acapacitor constructed according to the present invention includes anadhesion layer, a conductor in contact with the adhesion layer andhaving a thickness of less than six hundred Angstroms, a secondconductor, and a dielectric between the first and second conductors.

[0011] The present invention is also directed towards structures whereiniridium or rhodium may be used in place of the combination of theadhesion layer and conductor.

[0012] The present invention solves problems experienced with the priorart because it allows for the formation of thin films, such as platinum,without wetting effects. Those and other advantages and benefits of thepresent invention will become apparent from the description of thepreferred embodiments hereinbelow.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWING

[0013] For the present invention to be clearly understood and readilypracticed, the present invention will be described in conjunction withthe following figures, wherein:

[0014]FIG. 1 is a cross-sectional view of a structure constructedaccording to the teachings of the present invention;

[0015]FIG. 2 is a cross-sectional view of a capacitor in an early stageof fabrication according to the teachings of the present invention;

[0016]FIG. 3 is a cross-sectional view of the capacitor of FIG. 2 afterthe adhesion layer and conductor are removed from the top surface of thesubstrate;

[0017]FIG. 4 is a cross-sectional view of the capacitor of FIG. 3 aftera portion of the substrate is removed from around the adhesion layer andconductor;

[0018]FIG. 5 is a cross-sectional view of the capacitor of FIG. 4 afterthe exposed portion of the adhesion layer is removed;

[0019]FIG. 6 is a cross-sectional view of the capacitor of FIG. 5 aftera dielectric is formed on the conductor;

[0020]FIG. 7 is a cross-sectional view of the capacitor of FIG. 6 aftera second conductor is formed on the dielectric;

[0021]FIG. 8 is a cross-sectional view of a capacitor having adielectric and second conductor formed only within the conductor andwherein the adhesion layer is not removed;

[0022]FIG. 9 is a cross-sectional view of the capacitor of FIG. 8 afteran additional layer is formed over the capacitor;

[0023]FIG. 10 is a cross-sectional view of a post capacitor in an earlystage of fabrication according to the teachings of the presentinvention;

[0024]FIG. 11 is a cross-sectional view of the capacitor of FIG. 10after an adhesion layer and a conductor are formed on the post;

[0025]FIG. 12 is a cross-sectional view of the capacitor of FIG. 11after a dielectric layer and a second conductor are formed on theadhesion layer and the conductor;

[0026]FIG. 13 is a cross-sectional view of the capacitor of FIG. 12after portions of the adhesion layer, conductor, dielectric layer, andsecond conductor are removed;

[0027]FIG. 14 is a cross-sectional view of the capacitor of FIG. 13after an additional layer is formed over the capacitor; and

[0028]FIG. 15 is a block diagram of a system including devicesconstructed according to the teachings of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

[0029] It is to be understood that the figures and descriptions of thepresent invention have been simplified to illustrate elements that arerelevant for a clear understanding of the present invention whileeliminating, for purposes of clarity, other elements. Those of ordinaryskill in the art will recognize that other elements may be desirableand/or required in order to implement the present invention. However,because such elements are well known in the art, and because they do notfacilitate a better understanding of the present invention, a discussionof such elements is not provided herein.

[0030] Advantages of the present invention may be realized using anumber of structures and technologies, such as doped silicon substrate,silicon-on-insulator, silicon-on-sapphire, and thin film transistor. Theterm substrate, as used herein, shall mean one or more layers orstructures which may include active or operable portions of asemiconductor device formed on or in the substrate. A substrate isoften, but not always, the lowest layer of material.

[0031]FIG. 1 is a cross-sectional view of a conductive structure 10constructed in accordance with the present invention. The structure 10includes an adhesion layer 12 and a conductor 14 in contact with theadhesion layer 12, both of which are formed on a substrate 16. Asdiscussed hereinbelow, the structure 10 may take many forms such as, forexample, electrical contacts and capacitors. The illustrated embodimentmay be used, for example, as an electrical contact in an integratedcircuit, such as may be used with an interconnect or with a die bondpad.

[0032] The adhesion layer 12 adheres to both the substrate 16 and theconductor 14, and has desirable properties when exposed to subsequentprocessing steps such as annealing. The adhesion layer 12 may be, forexample, titanium, titanium nitride, tungsten carbide, tantalum nitride,tungsten nitride, noble metals, such as rhodium, iridium, osmium, andpalladium; noble metal oxides, such as ruthenium oxide, rhodium oxide,iridium oxide, and osmium oxide; and silicides of those materials. Thosematerials adhere well to typical substrate materials, adhere well totypical conductors, and are generally unaffected by processing stepssuch as annealing.

[0033] The adhesion layer 12 may be formed by, for example, chemicalvapor deposition (“CVD”). For an embodiment where the adhesion layer 12is titanium nitride, the CVD process may be accomplished with a pressureof 0.5 torr, a deposition temperature of about 560° C., a flow rate ofabout 25 sccm of NH₃, a flow rate of about 25 sccm of nitrogen, and aflow rate of about 50 sccm of a carrier gas. Alternatively, the adhesionlayer 12 may be formed, for example, by physical vapor deposition, suchas sputter deposition, co-sputter deposition, evaporation deposition,and co-evaporation deposition. Once deposited, the adhesion layer 12 maybe patterned as desired by, for example, conventional patterningtechniques. Examples of conventional patterning techniques includelithography, etching (chemical or mechanical), and chemical mechanicalpolishing (“CMP”).

[0034] The conductor 14 may be almost any conductor, including noblemetals and noble metal oxides such as, for example, platinum, ruthenium,iridium, rhodium, palladium, osmium, oxides of those metals, andsilicides of those metals. The conductor may have a thickness of lessthan six hundred (600) Angstroms. The conductor 14 will not exhibit“spotting” or “non-wetting” characteristics, even with a thickness ofless than six hundred (600) Angstroms, because the adhesion layer 12,particularly the above-identified adhesion materials, causes theconductor 14 to form a conformal layer on the adhesion layer 12.

[0035] The conductor 14 may be formed, for example, by CVD andsputtering. For an embodiment where the conductor 14 is platinum andformed by CVD, the flow rate of the carrier gas may be about 10 to 5000sccm, the deposition pressure may be about 0.4 to 10 torr, and thedeposition temperature about 100° C. to 500° C. The CVD process may beperformed without plasma enhancement, and diluent gas, such as nitrogenor argon, may be provided into the reaction chamber at a rate of up toabout 500 sccm.

[0036] Once formed, the structure 10 may be annealed to aid causing theconductor 14 to form in a conformal layer on the adhesion layer 12. Theannealing may be performed at a pressure of about 0.1 millitorr to about5 atmospheres and at a temperature of about 650° C. or greater, but at atemperature less than the melting point of the substrate 16. The annealmay be performed for a time period of about 30 to 300 seconds. Further,the anneal may be performed while the structure 10 is present in a gasenvironment, such as in an atmosphere of oxygen, ozone, argon, nitrogen,helium, and a combination thereof. Once annealed, the conductor 14 formsdirectly on the patterned adhesion layer 12.

[0037] The anneal may be, for example, a rapid thermal oxidation (RTO)anneal or a rapid thermal nitridation (RTN) anneal. For a RTO anneal,the temperature may be 700-800° C. for a time period of approximately30-60 seconds at 1 atm oxygen. For a RTN anneal, the temperature may be700-800° C. for a time period of 30-60 seconds at 1 atm nitrogen.

[0038] Conductor material which is deposited on the substrate 16 and noton the adhesion layer 12 during deposition of the conductor 14 may beremoved by exposing the structure 10 in a rinsing composition for asufficient time period to remove the conductor material. Examples ofsuitable rinsing compositions include water, aqua regia, hydrofluoricacid, hydrophilic acid, hydrogen peroxide, and a combination thereof.The rinsing may be performed for a time period of about 5 minutes orless in a conventional ultrasonic bath.

[0039] The substrate 16 may be any of many materials, such as, forexample, borophosphosilicate glass (“BPSG”), silicon dioxide, galliumarsenide, and Al₂O₃, and may be formed, for example, by CVD.

[0040] It has been found that iridium and rhodium offer superiorcharacteristics that resist spotting. As a result, iridium or rhodiummay be used to form a thin film less than six hundred Angstroms thick,without the spotting problems often associated with such thin films.Iridium or rhodium may be used in place of the combination of theadhesion layer 12 and the conductor 14 described herein. For example,and with reference to FIG. 1, iridium or rhodium may be used to form aconductive adhesion layer 12 that may be used without the conductor 14.Alternatively, iridium or rhodium may be used to form a conductor 14that may be used without the adhesion layer 12.

[0041]FIG. 2 is a cross-sectional view of one embodiment of thestructure 10 in an early stage of being fabricated into a capacitor. Theadhesion layer 12 and conductor 14 are formed in an opening 20 in thesubstrate 16. The opening 20 may be formed, for example, by selectivelymasking the substrate 16 so that only the portion of the substrate 16where the opening 20 is to be formed is exposed, by selectively andanisotropically etching the substrate 16 to form the opening 20, andthen removing the mask. A conductive interconnect 22 may also be formedunder the adhesion layer 12 to electrically connect the adhesion layer12 and conductor 14 to another part of the device in which the structure10 is formed. The interconnect 22 may be formed in a manner similar tothat used to form the opening 20. The interconnect 22 may also include acontact 24 that has a lower resistance than the interconnect 22. In thecase of the capacitor in the illustrated embodiment, the interconnect 22and contact 24 may provide current to and from the conductor 14, whichwill form a plate and store charge in the capacitor. The interconnect 22may be, for example, doped polysilicon, and the contact 24 may be, forexample, selected from a group including TiN, Rhodium, Ruthenium, andIridium.

[0042]FIG. 3 is a cross-sectional view of the structure 10 after theadhesion layer 12 and the conductor 14 have been removed from the topsurface of the substrate 16. The removal may be performed by, forexample, either a wet etch or a dry etch. In those examples, the opening20 may be filled with a protective material, such as photoresist, toprevent the adhesion layer 12 and the conductor 14 from being etched.After the etch is completed, the protective material may be removed fromthe opening 20. Because some materials, such as platinum, are difficultto etch, a mechanical abrasion step, such as CMP, may be used to removethe adhesion layer 12 and conductor 14 from the top surface of thesubstrate 16. In that example, a protective material may be used to fillthe opening 20 to prevent materials removed by the CMP from falling intothe opening 20.

[0043]FIG. 4 is a cross-sectional view of the structure 10 after aportion of the substrate 16 has been removed to expose vertical portionsof the adhesion layer 12 and of the conductor 14. The substrate 16 maybe removed by, for example, an etch that is selective to the substrate16 but which does not etch the adhesion layer 12 and the conductor 14.

[0044]FIG. 5 is a cross-sectional view of the structure 10 after theexposed portion of the adhesion layer 12 is removed. The adhesion layer12 may be removed with, for example, either a wet or a dry etch.

[0045]FIG. 6 is a cross-sectional view of the structure 10 after adielectric 30 is formed on the conductor 14. The dielectric 30 is shownbeing formed on both sides of the conductor 14, although as describedhereinbelow, the dielectric 30 may be formed on only one side of theconductor 14. The dielectric 30 may be, for example, selected from agroup including Ta₂O₅, barium strontium titanate (“BST”), strontiumtitanate (“ST”), Nb₂O₅, Y₂O₃, Ba(ZrTi)O₃, TiO₂, ZrO₂, and SrTiO₃. Thedielectric 30 may be formed, for example, by forming a layer of thedielectric 30 on the entire surface, and then selectively removing thedielectric 30 so that it remains only where desired. For example, thedielectric 30 may deposited over the entire surface by either sputteringor CVD, the dielectric 30 masked on both sides of the conductor 14 withphotoresist, and the exposed dielectric removed with a selective etch.

[0046]FIG. 7 is a cross-sectional view of the structure 10 after asecond conductor 32 is formed over the dielectric 30, thereby forming acapacitor. The second conductor 32 may be formed from the same orsimilar materials as the conductor 14 and in a manner similar to thatused to form the dielectric 30. A greater variety of materials may beused for the second conductor 32 because the second conductor 32 may notbe subject to extreme processing steps. For example, the secondconductor 32 may be formed after the last high temperature processingstep is completed. Examples of materials that may be used to form thesecond conductor 32 include platinum, ruthenium, iridium, rhodium,titanium nitride, tantalum nitride, tungsten nitride, aluminum, RhO₂,RuO₂, and Pd.

[0047] Many variations of the present invention are possible. Forexample, the structure may be formed without removing the adhesion layer12. Also, the dielectric 30 and second conductor 32 may be formed ononly one side of the conductor 14. Some embodiments will be describedhereinbelow.

[0048]FIG. 8 is a cross-sectional view of an embodiment of the structure10 wherein the dielectric 30 and the second conductor 32 have beenformed within the conductor 14 and the adhesion layer 12 is not removed.The adhesion layer's 12 effectiveness as an oxygen barrier is one factorthat may be used to determine whether to remove the adhesion layer 12.If the adhesion layer 12 is a good oxygen barrier, Rh/Rho₂ is one suchexample, it may be left on the conductor 14, as illustrated in FIG. 8.

[0049]FIG. 9 is a cross-sectional view of the structure 10 after anadditional layer 40 is formed. The additional layer 40 may be used toseparate the structure 10 from whatever may be formed above thestructure 10. The additional layer 40 may be formed, for example, by aCVD process and from the same materials used to form the substrate 16.The additional layer 40 may be planarized, such as by CMP, and aninterconnect 42 may be formed in the additional layer 40 to connect thesecond conductor 32 to another portion of the device in which thecapacitor 10 is formed. As with the interconnect 22, the interconnect 42may include a contact 44.

[0050]FIG. 10 is a cross-sectional view of a post 46 that will be usedto form a post capacitor in accordance with the present invention. Thepost 46 may be formed, for example, by filling an opening in a temporarylayer and then removing the temporary layer to leave the post 46. Thepost 46 may be formed from many materials such as, for example,polysilicon.

[0051]FIG. 11 is a cross-sectional view of the structure 10 after theadhesion layer 12 and the conductor 14 are formed over the post 46. Theadhesion layer 12 is formed before the conductor 14, and both may beformed in a manner such as described hereinabove.

[0052]FIG. 12 is a cross-sectional view of the structure 10 after thedielectric 30 and the second conductor 32 are formed over the post 46.The dielectric 30 is formed before the second conductor 32, and both maybe formed in a manner such as described hereinabove.

[0053]FIG. 13 is a cross-sectional view of the structure 10 after theadhesion layer 12, the conductor 14, the dielectric 30, and the secondconductor 32 are partially removed to leave a capacitor formed on thepost 46. The removal may be performed such as, for example, by forming amask over the portion to remain, etching the exposed portion of theadhesion layer 12, the conductor 14, the dielectric 30, and the secondconductor 32, and removing the mask to leave the capacitor. The mask maybe, for example, photoresist.

[0054]FIG. 14 is a cross-sectional view of the structure 10 after anadditional layer 40 has been formed over the capacitor. The additionallayer 40 may be planarized, such as by CMP, and an interconnect 42 maybe formed in the additional layer 40 to connect the second conductor 32to another portion of the device in which the capacitor 10 is formed.The interconnect 42 may also include a contact 44. An interconnect 22may also be formed to connect the adhesion layer 12 and the conductor 14to another portion of the device in which the capacitor is formed. Theinterconnect 22 to the adhesion layer 12 is formed prior to theformation of the adhesion layer 12, the conductor 14, the dielectric 30,and the second conductor 32, in a manner similar to the interconnect 22illustrated in FIG. 2.

[0055]FIG. 15 is a high level block diagram illustrating a system 50including a first device 52, a bus 54, and a second device 56. Thesystem 50 may be, for example, a memory system or a computer system. Thefirst device 52 may be a processor, and the second device 56 may be amemory. The first device 52 and the second device 56 may communicate viathe bus 54. The first and second devices 52, 56 may include structures10, such as capacitors and contacts, constructed according to theteaching of the present invention.

[0056] The present invention also includes a method of formingstructures and devices, such as capacitors. The method includes formingan adhesion layer 12 and forming a conductor 14 having a thickness ofless than six hundred Angstroms on the adhesion layer 12. The adhesionlayer 12 and the conductor 14 may be formed as described hereinbefore.When forming a capacitor, the method includes forming an adhesion layer12, forming a conductor 14 having a thickness of less than six hundredAngstroms on the adhesion layer 12, forming a second conductor 32, andforming a dielectric 30 between the conductor 14 and the secondconductor 32. The method may be used to form different types ofcapacitors, including post capacitors. When forming a post capacitor,the method may include forming the adhesion layer 12 on a post 46.Alternatively, the method may include forming the adhesion layer 12 inan opening 20. The adhesion layer 12 may have a first side and a secondside, and the method may includes forming the conductor 14 on one of thefirst and second sides of the adhesion layer 12. Alternatively, themethod may include forming the conductor 14 on both the first side ofthe adhesion layer 12 and on the second side of the adhesion layer 12,thereby increasing the capacitance of the capacitor.

[0057] An example of a method of forming a post capacitor according tothe present invention includes providing a substrate 16, forming a post46 on the substrate 16, forming an adhesion layer 12 on the post 46,forming a conductor 14 having a thickness of less than six hundredAngstroms on the adhesion layer 12, forming a second conductor 32, andforming a dielectric 30 between the conductor 14 and the secondconductor 32.

[0058] An example of a method of forming a capacitor in an opening 20includes providing a substrate 16, forming an opening 20 in thesubstrate 16, forming an adhesion layer 12 in the opening 20, forming aconductor 14 having a thickness of less than six hundred Angstroms onthe adhesion layer 12, forming a second conductor 32, and forming adielectric 30 between the conductor 14 and the second conductor 32.

[0059] Those of ordinary skill in the art will recognize that manymodifications and variations of the present invention may beimplemented. For example, one of the interconnects 22, 42 may be omittedand the corresponding conductor may be left to “float”. In addition,iridium or rhodium may be used in place of the combination of adhesionlayer 12 and conductor 14. The foregoing description and the followingclaims are intended to cover all such modifications and variations.

1. A conductive structure, comprising: an adhesion layer; and aconductor in contact with said adhesion layer and having a thickness ofless than six hundred Angstroms.
 2. The structure of claim 1, whereinsaid adhesion layer is selected from a group consisting of titanium,titanium alloys, noble metals, noble metal oxides, and silicides oftitanium, titanium alloys, and noble metal.
 3. The structure of claim 1,wherein said adhesion layer is selected from a group consisting oftitanium, titanium nitride, tungsten carbide, tantalum nitride, tungstennitride, rhodium, iridium, osmium, palladium, ruthenium oxide, rhodiumoxide, iridium oxide, osmium oxide, and silicides of titanium, titaniumnitride, tungsten carbide, tantalum nitride, tungsten nitride, rhodium,iridium, osmium, and palladium.
 4. The structure of claim 1, whereinsaid conductor is selected from a group consisting of noble metals,noble metal oxides, and silicides of noble metals.
 5. The structure ofclaim 4, wherein said conductor is selected from a group consisting ofplatinum, ruthenium, iridium, rhodium, palladium, and osmium; oxides ofplatinum, ruthenium, iridium, rhodium, palladium, and osmium; andsilicides of platinum, ruthenium, iridium, rhodium, palladium, andosmium.
 6. The structure of claim 1, wherein said adhesion layer is incontact with a substrate.
 7. The structure of claim 1, wherein saidadhesion layer is in contact with a material including silicon.
 8. Thestructure of claim 7, wherein said material including silicon isselected from a group consisting of silicon dioxide andborophosphosilicate glass.
 9. The structure of claim 1, wherein thestructure is part of a capacitor.
 10. The structure of claim 1, furthercomprising: a second conductor; and a dielectric between said conductorand said second conductor.
 11. A conductive structure, comprising: anadhesion layer; and a layer of platinum in contact with said adhesionlayer and having a thickness of less than six hundred Angstroms.
 12. Acapacitor, comprising: an adhesion layer; a first conductor in contactwith said adhesion layer and having a thickness of less than six hundredAngstroms; a second conductor; and a dielectric between said first andsecond conductors.
 13. The capacitor of claim 12, wherein said adhesionlayer is selected from a group consisting of titanium, titanium alloys,noble metals, noble metal oxides, and silicides of titanium, titaniumalloys, noble metals, and noble metal oxides.
 14. The capacitor of claim12, wherein said adhesion layer is selected from a group consisting oftitanium, titanium nitride, tungsten carbide, tantalum nitride, tungstennitride, rhodium, iridium, osmium, palladium, ruthenium oxide, rhodiumoxide, iridium oxide, osmium oxide, and silicides of titanium, titaniumnitride, tungsten carbide, tantalum nitride, tungsten nitride, rhodium,iridium, osmium, and palladium.
 15. The capacitor of claim 12, whereinsaid first conductor is selected from a group consisting of noblemetals, noble metal oxides, and silicides of noble metals.
 16. Thecapacitor of claim 15, wherein said first conductor is selected from agroup consisting of platinum, ruthenium, iridium, rhodium, palladium,and osmium; oxides of platinum, ruthenium, iridium, rhodium, palladium,and osmium; and silicides of platinum, ruthenium, iridium, rhodium,palladium, and osmium.
 17. The capacitor of claim 12, wherein saidsecond conductor is selected from a group consisting of aluminum,titanium nitride, tantalum nitride, tungsten nitride, platinum,ruthenium, iridium, rhodium, palladium, and osmium; oxides of platinum,ruthenium, iridium, rhodium, palladium, and osmium; and silicides ofplatinum, ruthenium, iridium, rhodium, palladium, and osmium.
 18. Thecapacitor of claim 12, wherein said dielectric is selected from a groupconsisting of Ta₂O₅, barium strontium titanate (“BST”), strontiumtitanate (“ST”), Nb₂O₅, Y₂O₃, Ba(ZrTi)O₃, TiO₂, ZrO₂, and SrTiO₃. 19.The capacitor of claim 12, wherein said adhesion layer is in contactwith a substrate.
 20. The capacitor of claim 12, wherein said adhesionlayer is in contact with a material including silicon.
 21. The capacitorof claim 20, wherein said material including silicon is selected from agroup consisting of silicon dioxide and borophosphosilicate glass. 22.The capacitor of claim 12, wherein said capacitor is selected from agroup consisting of a post capacitor and a trench capacitor.
 23. Acapacitor, comprising: a post; an adhesion layer in contact with saidpost; a first conductor in contact with said adhesion layer and having athickness of less than six hundred Angstroms; a second conductor; and adielectric between said first conductor and said second conductor.
 24. Acapacitor, comprising: a substrate; an adhesion layer defining anopening and in contact with said substrate; a first conductor in contactwith said adhesion layer and having a thickness of less than six hundredAngstroms; a second conductor; and a dielectric between said firstconductor and said second conductor.
 25. The capacitor of claim 24,wherein: said adhesion layer has an inside surface and an outsidesurface; and said first conductor is in contact with both said insidesurface and said outside surface of said adhesion layer.
 26. Thecapacitor of claim 24, wherein: said adhesion layer has an insidesurface and an outside surface; said first conductor is in contact withsaid inside surface of said adhesion layer but is not in contact withsaid outside surface of said adhesion layer; and said dielectric is incontact with said first conductor but is not in contact with saidoutside surface of said adhesion layer.
 27. A conductive structure,comprising: a substrate; and a layer of noble metal selected from thegroup consisting of iridium and rhodium, said layer having a thicknessof less than six hundred Angstroms and in contact with said substrate.28. The structure of claim 27, wherein said substrate includes silicon.29. The structure of claim 28, wherein said substrate is selected from agroup consisting of silicon diode and borophosphosilicate glass.
 30. Acapacitor, comprising: a substrate; a layer of noble metal selected fromthe group consisting of iridium and rhodium, said layer having athickness of less than six hundred Angstroms and in contact with saidsubstrate; a conductor; and a dielectric between said layer of noblemetal and said conductor.
 31. The capacitor of claim 30, wherein saidconductor is selected from a group consisting of aluminum, titaniumnitride, tantalum nitride, tungsten nitride, platinum, ruthenium,iridium, rhodium, palladium, and osmium; oxides of platinum, ruthenium,iridium, rhodium, palladium, and osmium; and silicides of platinum,ruthenium, iridium, rhodium, palladium, and osmium.
 32. The capacitor ofclaim 30, wherein said dielectric is selected from a group consisting ofTa₂O₅, barium strontium titanate (“BST”), strontium titanate (“ST”),Nb₂O₅, Y₂O₃, Ba(ZrTi)O₃, TiO₂, ZrO₂, and SrTiO₃.
 33. The capacitor ofclaim 30, wherein said substrate is selected from a group consisting ofsilicon dioxide and borophosphosilicate glass.
 34. A capacitor,comprising: a substrate forming a post; a layer of noble metal selectedfrom the group consisting of iridium and rhodium, said layer having athickness of less than six hundred Angstroms and in contact with saidpost; a conductor; and a dielectric between said layer of noble metaland said conductor.
 35. A capacitor, comprising: a substrate; a layer ofnoble metal selected from the group consisting of iridium and rhodium,said layer defining an opening, having a thickness of less than sixhundred Angstroms, and in contact with said substrate; a conductor; anda dielectric between said layer of noble metal and said conductor. 36.The capacitor of claim 35, wherein: said layer of noble metal has aninside surface and an outside surface; and said dielectric is in contactwith both said inside surface and said outside surface of said layer ofnoble metal.
 37. The capacitor of claim 35, wherein: said layer of noblemetal has an inside surface and an outside surface; and said dielectricis in contact with said inside surface of said layer of noble metal andis not in contact with said outside surface of said layer of noblemetal.
 38. A conductive structure, comprising; means for conductingelectromagnetic energy having a thickness of less than six hundredAngstroms; and means for adhering said means for conducting to asubstrate.
 39. The structure of claim 38, wherein said means foradhering is a layer selected from the group consisting of titanium,titanium alloys, noble metals, noble metal oxides, and silicides oftitanium, titanium alloys, and noble metal in contact with said meansfor conducting.
 40. The structure of claim 38, wherein said means forconducting is a conductor selected from the group consisting ofplatinum, ruthenium, iridium, rhodium, palladium, and osmium; oxides ofplatinum, ruthenium, iridium, rhodium, palladium, and osmium; andsilicides of platinum, ruthenium, iridium, rhodium, palladium, andosmium.
 41. The structure of claim 38, further comprising: second meansfor conducting electromagnetic energy; and means for insulating saidmeans for conducting from said second means for conducting.
 42. Thestructure of claim 41, wherein said means for insulating is a dielectricselected from the group consisting of Ta₂O₅, barium strontium titanate(“BST”), strontium titanate (“ST”) Nb₂O₅, Y₂O₃, Ba(ZrTi)O₃, TiO₂, ZrO₂,and SrTiO₃ between said first and second means for conducting.
 43. Acapacitor, comprising: first means for conducting electromagnetic energyhaving a thickness of less than six hundred Angstroms; means foradhering said first means for conducting to a substrate; second meansfor conducting electromagnetic energy; and means for insulating saidfirst means for conducting electromagnetic energy from said second meansfor conducting electromagnetic energy.
 44. The capacitor of claim 43,wherein said means for adhering is a layer selected from the groupconsisting of titanium, titanium alloys, noble metals, noble metaloxides, and suicides of titanium, titanium alloys, and noble metal incontact with said first means for conducting.
 45. The capacitor of claim43, wherein said first means for conducting is a conductor selected fromthe group consisting of platinum, ruthenium, iridium, rhodium,palladium, and osmium; oxides of platinum, ruthenium, iridium, rhodium,palladium, and osmium; and suicides of platinum, ruthenium, iridium,rhodium, palladium, and osmium.
 46. The capacitor of claim 43, whereinsaid means insulating is a dielectric selected from the group consistingof Ta₂O₅, barium strontium titanate (“BST”), strontium titanate (“ST”),Nb₂O₅, Y₂O₃, Ba(ZrTi)O₃, TiO₂, ZrO₂, and SrTiO₃ between said first andsecond means for conducting.
 47. A system, comprising: a bus; a firstdevice connected to said bus, said first device including a conductivestructure, said conductive structure having an adhesion layer and aconductor in contact with said adhesion layer, said conductor having athickness of less than six hundred Angstroms; and a second deviceconnected to said bus.
 48. The system of claim 47, wherein said seconddevice includes a second conductive structure, said second conductivestructure having a second adhesion layer and a second conductor incontact with said second adhesion layer, said second conductor having athickness of less than six hundred Angstroms.
 49. The system of claim47, wherein said first device is a processor.